Advanced machinery for testing fresh and hardened concrete including compression, coring, and non-destructive evaluation.
Used to extract cylindrical samples from hardened concrete structures for quality and compressive strength testing.
Provides precise cutting without vibrations, with controllable depth and speed, compliant with ASTM C42.
Used to precisely mix fresh concrete mix components in a laboratory environment before quality tests.
Ensures mix homogeneity up to 99%, enhancing the validity of test results.
Chemical analysis tools to estimate salt concentration (chloride/sulfate content) in mixing water, to avoid future reinforcement corrosion.
Reliable results with ±0.01% accuracy, compliant with BS 1008 specifications.
Used to precisely cut concrete samples to required dimensions for compression tests or visual inspection.
Equipped with high-quality diamond blades, providing smooth cutting without breaking or lateral cracks.
A standard tool used to measure the consistency and workability of fresh concrete (Slump Test).
Compliant with ASTM C143, gives a direct indicator of mix consistency and workability.
Used to form cylindrical concrete samples for compression testing at various ages.
Ensures a regular cylindrical shape with standard dimensions per ASTM C39, made from non-adhesive materials for easy sample removal.
Used to cure concrete samples underwater at constant temperatures ranging between (25 ± 3°C) to ensure ideal curing per ASTM C1064.
Equipped with digital thermal control ±1°C per ASTM C31.
High-pressure device used to determine the fracture stress resistance of concrete samples after time periods (7–28 days).
Load capacity up to 5000 KN, with calibration accuracy ±1%, compliant with ASTM C39.
Used to level the ends of concrete specimens by pouring sulfur mortar at a temperature compliant with standard specifications (130 to 145°C), ensuring ideal load distribution during testing.
Provides a smooth and level surface with a flatness ratio exceeding 99% per ASTM C617.
A precision measuring tool for fresh concrete temperature to ensure concrete mix quality during the casting process.
Precise reading up to ±0.1°C, suitable for international standard ASTM C1064.
Used to form 150×150 mm cubic samples for compression tests.
Made from stainless steel with a design that ensures dimensional accuracy per BS 1881.
Used to dry concrete samples or other materials before performing weight or moisture tests.
Equipped with digital temperature control up to 250°C, with uniform heat distribution ±1°C.
Used to estimate the compressive strength of hardened concrete by a non-destructive method, giving a quick indicator of concrete strength on site.
Gives preliminary results for compressive strength with low standard deviation when used on clean and flat surfaces per ASTM C805.
Used to determine the flowability of fresh concrete, applied mainly in self-compacting concrete (SCC).
Measurement is done using a standard circle and repeated drop of the metal disc, with mix spread diameter recorded to ±1 cm accuracy per ASTM C143.
Used to evaluate concrete homogeneity and detect honeycombing or voids within the concrete mass by measuring the propagation time of sound waves through transmitter and receiver electrodes.
Can detect internal defects with accuracy up to ±1 millisecond in pulse time, per ASTM C597.